Verwandte Artikel zu The Use Of Cold Sprayed Alloys For Metallic Stents
Inhaltsangabe
1- This study shows the ability to successfully cold-spray 316L stainless steel using nitrogen and helium as a propellant gas. The microstructure was characterized with low porosity and fine grain structure. In addition, after post-processing heat treatment, the microstructure became denser (i.e. lower porosity). The microhardness did not change with 400°C annealing temperature but decreased significantly at 800°C, which can be explained by the recrystallization that occurs during cold-spraying. Both the ductility and strength were improved after annealing at 1100°C, in particular. 2- This study shows the ability to successfully cold-spray composite 316L-CoCr using nitrogen as a propellant gas with Co-Cr volume fractions (i.e. 25%, 33.3%). The deposition efficiency decreased with increasing the amount of Co-Cr. The microstructure is characterized by low porosity level in the first two mixes. At 50% as mixed Co-Cr and 316L, the actual as coated material was 33% Co-Cr, due to difficulties in bonding Co-Cr particles to each other. Thus, the porosity was high at the 50% mixture and cracks were also apparent.
Die Inhaltsangabe kann sich auf eine andere Ausgabe dieses Titels beziehen.
Über die Autorin bzw. den Autor
Bandar Abdulaziz AlMangour,PhD Candidate in UCLA, Materials science and Engineering,M.Eng, McGill university, Materials Engineering, 2012 Research interests: understanding of the structure-property relationships, simulation & characterization of advanced structural metals in particular nanostructured alloys, manufacturing and materials processing
„Über diesen Titel“ kann sich auf eine andere Ausgabe dieses Titels beziehen.
Suchergebnisse für The Use Of Cold Sprayed Alloys For Metallic Stents
Foto des Verkäufers
The Use Of Cold Sprayed Alloys For Metallic Stents
Verlag:
LAP LAMBERT Academic Publishing Feb 2014, 2014
ISBN 10: 3848421577
ISBN 13: 9783848421572
Neu
Taschenbuch
Anbieter: BuchWeltWeit Ludwig Meier e.K., Bergisch Gladbach, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Taschenbuch. Zustand: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -1- This study shows the ability to successfully cold-spray 316L stainless steel using nitrogen and helium as a propellant gas. The microstructure was characterized with low porosity and fine grain structure. In addition, after post-processing heat treatment, the microstructure became denser (i.e. lower porosity). The microhardness did not change with 400°C annealing temperature but decreased significantly at 800°C, which can be explained by the recrystallization that occurs during cold-spraying. Both the ductility and strength were improved after annealing at 1100°C, in particular. 2- This study shows the ability to successfully cold-spray composite 316L-CoCr using nitrogen as a propellant gas with Co-Cr volume fractions (i.e. 25%, 33.3%). The deposition efficiency decreased with increasing the amount of Co-Cr. The microstructure is characterized by low porosity level in the first two mixes. At 50% as mixed Co-Cr and 316L, the actual as coated material was 33% Co-Cr, due to difficulties in bonding Co-Cr particles to each other. Thus, the porosity was high at the 50% mixture and cracks were also apparent. 112 pp. Englisch. Bestandsnummer des Verkäufers 9783848421572
Neu kaufen
EUR 54,90
EUR 23,00 Versand
Versand von Deutschland nach USA
Versand von Deutschland nach USA
Anzahl: 2 verfügbar
Foto des Verkäufers
The Use Of Cold Sprayed Alloys For Metallic Stents
Verlag:
LAP LAMBERT Academic Publishing, 2014
ISBN 10: 3848421577
ISBN 13: 9783848421572
Neu
Softcover
Anbieter: moluna, Greven, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Zustand: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Almangour BandarBandar Abdulaziz AlMangour,PhD Candidate in UCLA, Materials science and Engineering,M.Eng, McGill university, Materials Engineering, 2012 Research interests: understanding of the structure-property relationships, sim. Bestandsnummer des Verkäufers 5520998
Neu kaufen
EUR 45,45
EUR 48,99 Versand
Versand von Deutschland nach USA
Versand von Deutschland nach USA
Anzahl: Mehr als 20 verfügbar
Foto des Verkäufers
The Use Of Cold Sprayed Alloys For Metallic Stents
Verlag:
LAP LAMBERT Academic Publishing, 2014
ISBN 10: 3848421577
ISBN 13: 9783848421572
Neu
Taschenbuch
Anbieter: AHA-BUCH GmbH, Einbeck, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Taschenbuch. Zustand: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - 1- This study shows the ability to successfully cold-spray 316L stainless steel using nitrogen and helium as a propellant gas. The microstructure was characterized with low porosity and fine grain structure. In addition, after post-processing heat treatment, the microstructure became denser (i.e. lower porosity). The microhardness did not change with 400°C annealing temperature but decreased significantly at 800°C, which can be explained by the recrystallization that occurs during cold-spraying. Both the ductility and strength were improved after annealing at 1100°C, in particular. 2- This study shows the ability to successfully cold-spray composite 316L-CoCr using nitrogen as a propellant gas with Co-Cr volume fractions (i.e. 25%, 33.3%). The deposition efficiency decreased with increasing the amount of Co-Cr. The microstructure is characterized by low porosity level in the first two mixes. At 50% as mixed Co-Cr and 316L, the actual as coated material was 33% Co-Cr, due to difficulties in bonding Co-Cr particles to each other. Thus, the porosity was high at the 50% mixture and cracks were also apparent. Bestandsnummer des Verkäufers 9783848421572
Neu kaufen
EUR 62,49
EUR 35,00 Versand
Versand von Deutschland nach USA
Versand von Deutschland nach USA
Anzahl: 1 verfügbar
Foto des Verkäufers
The Use Of Cold Sprayed Alloys For Metallic Stents
Verlag:
LAP LAMBERT Academic Publishing Feb 2014, 2014
ISBN 10: 3848421577
ISBN 13: 9783848421572
Neu
Taschenbuch
Anbieter: buchversandmimpf2000, Emtmannsberg, BAYE, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Taschenbuch. Zustand: Neu. This item is printed on demand - Print on Demand Titel. Neuware -1- This study shows the ability to successfully cold-spray 316L stainless steel using nitrogen and helium as a propellant gas. The microstructure was characterized with low porosity and fine grain structure. In addition, after post-processing heat treatment, the microstructure became denser (i.e. lower porosity). The microhardness did not change with 400°C annealing temperature but decreased significantly at 800°C, which can be explained by the recrystallization that occurs during cold-spraying. Both the ductility and strength were improved after annealing at 1100°C, in particular. 2- This study shows the ability to successfully cold-spray composite 316L-CoCr using nitrogen as a propellant gas with Co-Cr volume fractions (i.e. 25%, 33.3%). The deposition efficiency decreased with increasing the amount of Co-Cr. The microstructure is characterized by low porosity level in the first two mixes. At 50% as mixed Co-Cr and 316L, the actual as coated material was 33% Co-Cr, due to difficulties in bonding Co-Cr particles to each other. Thus, the porosity was high at the 50% mixture and cracks were also apparent.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 112 pp. Englisch. Bestandsnummer des Verkäufers 9783848421572
Neu kaufen
EUR 54,90
EUR 60,00 Versand
Versand von Deutschland nach USA
Versand von Deutschland nach USA
Anzahl: 1 verfügbar
Foto des Verkäufers
The Use Of Cold Sprayed Alloys For Metallic Stents
Verlag:
LAP LAMBERT Academic Publishing, 2014
ISBN 10: 3848421577
ISBN 13: 9783848421572
Neu
Taschenbuch
Anbieter: preigu, Osnabrück, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Taschenbuch. Zustand: Neu. The Use Of Cold Sprayed Alloys For Metallic Stents | Bandar Almangour | Taschenbuch | 112 S. | Englisch | 2014 | LAP LAMBERT Academic Publishing | EAN 9783848421572 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu. Bestandsnummer des Verkäufers 105436352
Neu kaufen
EUR 47,95
EUR 70,00 Versand
Versand von Deutschland nach USA
Versand von Deutschland nach USA
Anzahl: 5 verfügbar