ISBN: 9783838356709 - stainless steels and ozone: the effect of dissolved ozone on the corrosion behaviour of stainless steels (9 Ergebnisse)

Zustand: New. pp. 100.

Taschenbuch. Zustand: Neu. Stainless steels and ozone | The effect of dissolved ozone on the corrosion behaviour of stainless steels | Antero Pehkonen | Taschenbuch | 100 S. | Englisch | 2010 | LAP LAMBERT Academic Publishing | EAN 9783838356709 | Verantwortliche Person für die EU: BoD - Books on Demand, In de Tarpen 42, 22848 Norderstedt, info[at]bod[dot]de | Anbieter: preigu.…

Paperback. Zustand: Like New. LIKE NEW. SHIPS FROM MULTIPLE LOCATIONS. book.

Taschenbuch. Zustand: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -The corrosion behaviour of several stainless steels and some pure metals has been investigated in water solutions with dissolved ozone. Dissolved ozone increases the redox-potential of solutions to about +1200 mV vs. SCE and the corrosion potential of stainless steel to the transpassive region. The corrosion rate of stainless steels increases as the amount of alloying elements increases. The corrosion of stainless steels is mainly general but also peeling of oxide layers and pitting was also observed. As the pH of the solution is decreased, the corrosion rate of higher alloyed steels increases at higher pH than lower alloyed steels. Dissolved ozone increases the thickness of the oxide layers greatly up to 260 nm and greatly changes the composition of the layer. Chromium concentration is negligible in the oxide layers. Molybdenum concentrates in the outer layer, even more so with lower alloyed steels. Iron and alloying elements have oxidised to their highest valencies. The main components in the oxide layers are iron oxides and on the surfaces also MoO6 occurs. 100 pp. Englisch.…

Taschenbuch. Zustand: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - The corrosion behaviour of several stainless steels and some pure metals has been investigated in water solutions with dissolved ozone. Dissolved ozone increases the redox-potential of solutions to about +1200 mV vs. SCE and the corrosion potential of stainless steel to the transpassive region. The corrosion rate of stainless steels increases as the amount of alloying elements increases. The corrosion of stainless steels is mainly general but also peeling of oxide layers and pitting was also observed. As the pH of the solution is decreased, the corrosion rate of higher alloyed steels increases at higher pH than lower alloyed steels. Dissolved ozone increases the thickness of the oxide layers greatly up to 260 nm and greatly changes the composition of the layer. Chromium concentration is negligible in the oxide layers. Molybdenum concentrates in the outer layer, even more so with lower alloyed steels. Iron and alloying elements have oxidised to their highest valencies. The main components in the oxide layers are iron oxides and on the surfaces also MoO6 occurs.…

Zustand: New. Print on Demand pp. 100 2:B&W 6 x 9 in or 229 x 152 mm Perfect Bound on Creme w/Gloss Lam.

Zustand: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Pehkonen AnteroM.Sc.(Tech.) 1984 at Helsinki University of Technology (today Aalto University), department of Materials Science. Five years in industry as a corrosion engineer and since 1990 as a senior reasearh scientist at Aalto Un.…

Zustand: New. PRINT ON DEMAND pp. 100.

Taschenbuch. Zustand: Neu. This item is printed on demand - Print on Demand Titel. Neuware -The corrosion behaviour of several stainless steels and some pure metals has been investigated in water solutions with dissolved ozone. Dissolved ozone increases the redox-potential of solutions to about +1200 mV vs. SCE and the corrosion potential of stainless steel to the transpassive region. The corrosion rate of stainless steels increases as the amount of alloying elements increases. The corrosion of stainless steels is mainly general but also peeling of oxide layers and pitting was also observed. As the pH of the solution is decreased, the corrosion rate of higher alloyed steels increases at higher pH than lower alloyed steels. Dissolved ozone increases the thickness of the oxide layers greatly up to 260 nm and greatly changes the composition of the layer. Chromium concentration is negligible in the oxide layers. Molybdenum concentrates in the outer layer, even more so with lower alloyed steels. Iron and alloying elements have oxidised to their highest valencies. The main components in the oxide layers are iron oxides and on the surfaces also MoO6 occurs.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 100 pp. Englisch.…