ISBN: 9786139967520 - advanced lithium ion batteries: synthesis of various cathode and anode material (5 Ergebnisse)

Taschenbuch. Zustand: Neu. Advanced Lithium Ion Batteries | Synthesis of Various Cathode and Anode Material | Madhu Mohan V. (u. a.) | Taschenbuch | 88 S. | Englisch | 2019 | LAP LAMBERT Academic Publishing | EAN 9786139967520 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu.…

Taschenbuch. Zustand: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware --MoO3 nanobelts and PEO surfactant MoO3 nanobelts were synthesized using simple hydrothermal method. The PEO surfactant MoO3 nanobelts have high specific capacity at the nineth cycle (64.2%) compared to pure MoO3 nanobelts (58.9%). The 12.5 wt% PEO surfactant MoO3 nanobelts show better stabilized specific capacity (218 mAhg-1) at the 25th cycle which is more than the pure MoO3 nanobelts (198 mAhg-1). -MoO3 nanobelts and PVP surfactant MoO3 nanobelts have been synthesized. The PVP surfactant MoO3 nanobelts has an initial specific capacity of 300 mAh/g, and its stabilized capacity still remained as high as 169 mAh/g after 50 cycles. The V2O5 nanotubes electrode battery shows initial specific capacity 192 mAhg-1, whereas the PEG surfactant V2O5 nanotubes exhibite 204 mAhg-1 with constant current density of 20 mAg-1 at 2.0-4.0 V versus Li/Li+ potential range. Single crystalline flowerlike -MoO3 NRs synthesised through a solvothermal method and tested NRs as anode material for a rechargeable LIB. The flowerlike -MoO3 NRs display high capacity of 1182 mAh g-1at a constant current density of 30 mA g-1. The capacity is still up to 695 mAh g-1after 189 cycles. 88 pp. Englisch.…

Taschenbuch. Zustand: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - -MoO3 nanobelts and PEO surfactant MoO3 nanobelts were synthesized using simple hydrothermal method. The PEO surfactant MoO3 nanobelts have high specific capacity at the nineth cycle (64.2%) compared to pure MoO3 nanobelts (58.9%). The 12.5 wt% PEO surfactant MoO3 nanobelts show better stabilized specific capacity (218 mAhg-1) at the 25th cycle which is more than the pure MoO3 nanobelts (198 mAhg-1). -MoO3 nanobelts and PVP surfactant MoO3 nanobelts have been synthesized. The PVP surfactant MoO3 nanobelts has an initial specific capacity of 300 mAh/g, and its stabilized capacity still remained as high as 169 mAh/g after 50 cycles. The V2O5 nanotubes electrode battery shows initial specific capacity 192 mAhg-1, whereas the PEG surfactant V2O5 nanotubes exhibite 204 mAhg-1 with constant current density of 20 mAg-1 at 2.0-4.0 V versus Li/Li+ potential range. Single crystalline flowerlike -MoO3 NRs synthesised through a solvothermal method and tested NRs as anode material for a rechargeable LIB. The flowerlike -MoO3 NRs display high capacity of 1182 mAh g-1at a constant current density of 30 mA g-1. The capacity is still up to 695 mAh g-1after 189 cycles.…

Kartoniert / Broschiert. Zustand: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: V. Madhu MohanDr. V. Madhu Mohan is working as Physics faculty member in the Rajiv Gandhi University of Knowledge Technologies, Andrapradesh, India. He did his postdoctoral research, Wuhan University of technology, PR China from July. …

Taschenbuch. Zustand: Neu. This item is printed on demand - Print on Demand Titel. Neuware -¿-MoO3 nanobelts and PEO surfactant MoO3 nanobelts were synthesized using simple hydrothermal method. The PEO surfactant MoO3 nanobelts have high specific capacity at the nineth cycle (64.2%) compared to pure MoO3 nanobelts (58.9%). The 12.5 wt% PEO surfactant MoO3 nanobelts show better stabilized specific capacity (218 mAhg¿1) at the 25th cycle which is more than the pure MoO3 nanobelts (198 mAhg¿1). ¿-MoO3 nanobelts and PVP surfactant MoO3 nanobelts have been synthesized. The PVP surfactant MoO3 nanobelts has an initial specific capacity of 300 mAh/g, and its stabilized capacity still remained as high as 169 mAh/g after 50 cycles. The V2O5 nanotubes electrode battery shows initial specific capacity 192 mAhg¿1, whereas the PEG surfactant V2O5 nanotubes exhibite 204 mAhg¿1 with constant current density of 20 mAg¿1 at 2.0-4.0 V versus Li/Li+ potential range. Single crystalline flowerlike ¿-MoO3 NRs synthesised through a solvothermal method and tested NRs as anode material for a rechargeable LIB. The flowerlike ¿-MoO3 NRs display high capacity of 1182 mAh g-1at a constant current density of 30 mA g-1. The capacity is still up to 695 mAh g-1after 189 cycles.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 88 pp. Englisch.…