Thanatcha wanichtanom (9 Ergebnisse)

Zustand: New.

Zustand: New.

paperback. Zustand: New. NEW. SHIPS FROM MULTIPLE LOCATIONS. book.

Taschenbuch. Zustand: Neu. The Shear Bond Strength Of Lithium Disilicate Glass | Ceramic Bonded With Titanium Using Four Resin Cements | Thanatcha Wanichtanom (u. a.) | Taschenbuch | 76 S. | Englisch | 2014 | Scholars' Press | EAN 9783639667998 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu. …

Taschenbuch. Zustand: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -The purpose of this experimental study was to determine and compare the shear bond strength of pressed lithium disilicate ceramic bonded with titanium disc by using four cements; Multilink implant® (MI), RelyX unicem® (RU), Panavia F2® (PF) and Superbond C&B® (SB). Sixty pressed lithium disilicate discs were luted to 60 titanium discs with 1 of 4 luting cements. The bonded materials were subjected for shear bond strength testing by a universal testing machine. Comparison of mean shear bond strength was evaluated by one-way ANOVA and t-test analysis. Shear bond strength of each cement ranked from the highest to the lowest are following; MI was 58.27±2.05 MPa, RU was 45.81±1.88 MPa, SB was 39.55±2.29 MPa, and PF was 39.42±2.11 MPa. Significant differences were observed statistically among groups (p0.001), except SB and PF. 76 pp. Englisch. …

Zustand: New. Print on Demand.

Zustand: New. PRINT ON DEMAND.

Taschenbuch. Zustand: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - The purpose of this experimental study was to determine and compare the shear bond strength of pressed lithium disilicate ceramic bonded with titanium disc by using four cements; Multilink implant® (MI), RelyX unicem® (RU), Panavia F2® (PF) and Superbond C&B® (SB). Sixty pressed lithium disilicate discs were luted to 60 titanium discs with 1 of 4 luting cements. The bonded materials were subjected for shear bond strength testing by a universal testing machine. Comparison of mean shear bond strength was evaluated by one-way ANOVA and t-test analysis. Shear bond strength of each cement ranked from the highest to the lowest are following; MI was 58.27±2.05 MPa, RU was 45.81±1.88 MPa, SB was 39.55±2.29 MPa, and PF was 39.42±2.11 MPa. Significant differences were observed statistically among groups (p0.001), except SB and PF.…

Taschenbuch. Zustand: Neu. This item is printed on demand - Print on Demand Titel. Neuware -The purpose of this experimental study was to determine and compare the shear bond strength of pressed lithium disilicate ceramic bonded with titanium disc by using four cements; Multilink implant® (MI), RelyX unicem® (RU), Panavia F2® (PF) and Superbond C&B® (SB). Sixty pressed lithium disilicate discs were luted to 60 titanium discs with 1 of 4 luting cements. The bonded materials were subjected for shear bond strength testing by a universal testing machine. Comparison of mean shear bond strength was evaluated by one-way ANOVA and t-test analysis. Shear bond strength of each cement ranked from the highest to the lowest are following; MI was 58.27±2.05 MPa, RU was 45.81±1.88 MPa, SB was 39.55±2.29 MPa, and PF was 39.42±2.11 MPa. Significant differences were observed statistically among groups (pVDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 76 pp. Englisch. …